abstract

• A medium Mn steel (MMS) was cast by employing a vacuum induction furnace. After that, the steel was hot rolled (HR) in order to achieve a final thickness of 1.4 mm. The microstructure of the sheet was found to be composed of martensite and a little amount of austenite, the Ultimate Tensile Strength (UTS in this processing condition was close to 1600 MPa and a negligible elongation was found. An intercritical annealing (IA) heat treatment was applied to the steel to promote the austenite reversion and increase its amount and stability. Previous thermodynamic simulations and experimental results were used to determine the temperature and time parameters of the IA. After the steel was subjected to this heat treatment, it exhibited an elongation close to 35%25 and an UTS close to 1100 MPa. Bendability testing was carried out in that condition in order to correlate it with the microstructural changes in the sheet. It was found that the critical bending angle was higher in the IA condition in comparison with the HR state.

authors

• Garay-Reyes C.G.
• Hernández Rivera José Luis
• Ramos Azpeitia Mitsuo Osvaldo

publication date

• 2023-01-01

published in

• IOP Conference Series: Materials Science and Engineering  Proceedings

keywords

Digital Object Identifier (DOI)

• 10.1088/1757-899X/1284/1/012030

PubMed ID

start page

end page

volume

• 1284

issue